Lithium tantalate (LiTaO3), has properties which make it useful for SAW (surface acoustic wave) devices and, to a different specification, for optical use. Wafers can be produced with varying properties, such as "black" wafers free of pyroelectric discharge, 4" (100mm), orientation 36°, 39°, 42 °, 46°, 48°, X-CUT ... detailed specifications, or with higher physical strength to withstand processing during manufacture, resulting in higher yields.
 |
| Diameter |
Reference Flat Perpendicular to |
Thickness |
Surface Finish |
|||
36° Y - Cut |
76.2 ± 0.7 (mm) |
22 ± 3 (mm) |
X |
0.35 ± 0.03 (mm) |
Front |
Mirror Polished |
42° Y - Cut |
X |
0.50 ± 0.03 (mm) |
||||
X - Cut |
100.0 ± 0.7 (mm) |
32 ± 3 (mm) |
Parallel to 112.2° Y |
0.50 ± 0.03 (mm) |
Back |
Ground |
|
Section
|
|
 |
|
|
| Diameter |
Reference Flat Perpendicular to |
Sub Flat |
Thickness |
Surface Finish |
||||
Z - Cut |
50.8 ± 0.7 (mm) |
21 ± 3 (mm) |
Y |
10 ± 3(mm) |
- X |
0.50 ± 0.03 (mm) |
Front |
Mirror Polished |
Back |
||||||||
 |
Reproduced by kind permission ofYamaju Ceramics Co., Ltd. . © Yamaju 2004 Specifications subject to change without notice. All rights reserved Roditi International 2007